UNDER WATER WELDING

 

 

CONTENTS

n  INTRODUCTION

n  HISTORY

n  CLASSIFICATION

n  PRINCIPLE OF OPERATIONS

n  BLOCK DIAGRAM

n  ADVANTAGES

n  DISADVANTAGES

n  APPLICATIONS

n  CONCLUSION

n  REFERENCES

 

INTRODUCTION

            Underwater welding is a type of welding which takes place underwater. A number of different welding techniques can be used underwater, with arc welding being among the most common. There are numerous applications for underwater welding skills, including repairing ships, working on oil platforms, and maintaining underwater pipelines. People with skills and experience in this field can find employment all over the world.

            In underwater welding, the environment around the welder is wet. He or she wears a dive suit, and uses welding equipment which has been customized for wet environments. This equipment is designed to be as safe as possible for the welder, reducing the risk of electric shock and the development of dangerous situations. Someone who practices underwater welding must be both a skilled welder and a skilled diver, with the ability to safely and effectively prepare a scene for welding and to confirm that the welds are of high quality.

HISTORY

            The fact that electric arc could operate was known for over a 100 years. The first ever underwater welding was carried out by British Admiralty – Dockyard for sealing leaking ship rivets below the water line.

 

            Underwater welding is an important tool for underwater fabrication works. In 1946, special waterproof electrodes were developed in Holland by ‘Van der Willingen’. In recent years the number of offshore structures including oil drilling rigs, pipelines, platforms are being installed significantly. Some of these structures will experience failures of its elements during normal usage and during unpredicted occurrences like storms, collisions. Any repair method will require the use of underwater welding.

CLASSIFICATION

    Underwater welding can be classified as

 

1. Wet Welding:

     In wet welding the welding is performed underwater, directly exposed to the wet environment

 

2. Dry Welding:

     In dry welding, a dry chamber is created near the area to be welded and the welder does the job by staying inside the chamber.

WET WELDING

            Wet Welding indicates that welding is performed underwater, directly exposed to the wet environment. A special electrode is used and welding is carried out manually just as one does in open air welding. The increased freedom of movement makes wet welding the most effective, efficient and economical method. Welding power supply is located on the surface with connection to the diver/welder via cables and hoses.

 

            In wet welding MMA (Manual metal arc welding) is used.

 

How the power supply is used in wet welding:
Power supply        : DC
Polarity                  : -ve polarity

When DC is used with +ve polarity, electrolysis will take place and cause rapid deterioration of any metallic components in the electrode holder. For wet welding AC is not used on account of electrical safety and difficulty in maintaining an arc underwater. 
The power source should be a direct current machine rated at 300 or 400 amperes. Motor generator welding machines are most often used for underwater welding in the wet. The welding machine frame must be grounded to the ship. The welding circuit must include a positive type of switch, usually a knife switch operated on the surface and commanded by the welder-diver. The knife switch in the electrode circuit must be capable of breaking the full welding current and is used for safety reasons. The welding power should be connected to the electrode holder only during welding.
Direct current with electrode negative (straight polarity) is used. Special welding electrode holders with extra insulation against the water are used. The underwater welding electrode holder utilizes a twist type head for gripping the electrode. It accommodates two sizes of electrodes.
The electrode types used conform to AWS E6013 classification. The electrodes must be waterproofed. All connections must be thoroughly insulated so that the water cannot come in contact with the metal parts. If the insulation does leak, seawater will come in contact with the metal conductor and part of the current will leak away and will not be available at the arc. In addition, there will be rapid deterioration of the copper cable at the point of the leak.

BLOCK DIAGRAM OF WET WELDING

WORKING PRINCIPLE OF WET WELDING

            The process of underwater wet welding takes in the following manner:

 

            The work to be welded is connected to one side of an electric circuit, and a metal electrode to the other side. These two parts of the circuit are brought together, and then separated slightly. The electric current jumps the gap and causes a sustained spark (arc), which melts the bare metal, forming a weld pool. At the same time, the tip of electrode melts, and metal droplets are projected into the weld pool. During this operation, the flux covering the electrode melts to provide a shielding gas, which is used to stabilize the arc column and shield the transfer metal. The arc burns in a cavity formed inside the flux covering, which is designed to burn slower than the metal barrel of the electrode.

ADVANTAGES OF WET WELDING

     Wet underwater MMA welding has now been widely used for many years in the repair of offshore platforms. The benefits of wet welding are: -

 

•         The versatility and low cost of wet welding makes this method

•         Other benefits include the speed. With which the operation is carried out.

•         It is less costly compared to dry welding.

•         The welder can reach portions of offshore structures that could not be welded using other methods.

•         No enclosures are needed and no time is lost building. Readily available standard welding machine and equipments are used. The equipment needed for mobilization of a wet welded job is minimal.

DISADVANTAGES OF WET WELDING

     There is rapid quenching of the weld metal by the surrounding water. Although quenching increases the tensile strength of the weld, it decreases the ductility and impact strength of the weldment and increases porosity and hardness.

 

•         Hydrogen Embrittlement – Large amount of hydrogen is present in the weld region, resulting from the dissociation of the water vapour in the arc region. The H2 dissolves in the Heat Affected Zone (HAZ) and the weld metal, which causes Embrittlement, cracks and microscopic fissures. Cracks can grow and may result in catastrophic failure of the structure.

 

•         Another disadvantage is poor visibility. The welder some times is not able to weld properly.

HYPERBARIC WELDING
(DRY WELDING)

            Hyperbaric welding is carried out in chamber sealed around the structure o be welded. The chamber is filled with a gas (commonly helium containing 0.5 bar of oxygen) at the prevailing pressure. The habitat is sealed onto the pipeline and filled with a breathable mixture of helium and oxygen, at or slightly above the ambient pressure at which the welding is to take place. This method produces high-quality weld joints that meet X-ray and code requirements. The gas tungsten arc welding process is employed for this process. The area under the floor of the Habitat is open to water. Thus the welding is done in the dry but at the hydrostatic pressure of the sea water surrounding the Habitat.

BLOCK DIAGRAM OF DRY WELDING

ADVANTAGES OF DRY WELDING

1. Welder/Diver Safety – Welding is performed in a chamber, immune to ocean currents and marine animals. The warm, dry habitat is well illuminated and has its own environmental control system (ECS).

 

2. Good Quality Welds – This method has ability to produce welds of quality comparable to open air welds because water is no longer present to quench the weld and H2 level is much lower than wet welds.

 

3. Surface Monitoring – Joint preparation, pipe alignment, NDT inspection, etc. are monitored visually.

 

4. Non-Destructive Testing (NDT) – NDT is also facilitated by the dry habitat environment.

DISADVANTAGES OF DRY WELDING

1. The habitat welding requires large quantities of complex equipment and much support equipment on the surface. The chamber is extremely complex.

 

2. Cost of habitat welding is extremely high and increases with depth. Work depth has an effect on habitat welding. At greater depths, the arc constricts and corresponding higher voltages are required. The process is costly – a $ 80000 charge for a single weld job. One cannot use the same chamber for another job, if it is a different one.

APPLICATIONS

•               Underwater welding provides a means of assembly or repair underwater. Alternatives, which include clamped and grouted repairs (which may introduce unacceptably high loading on offshore structures), and the use of bolted flanges for tie-ins, are not necessarily always satisfactory.

•               Underwater welding techniques are most commonly used in executing marine engineering projects such as installation of oil and gas rigs. Underwater welding is mostly related to welding work pieces made from different types of metals such as steel, aluminum, copper, and others.

•               Underwater welding techniques are used for welding steel pipelines, other offshore structures, submerged parts of large ships, and underwater structures supporting a harbor

RISKS INVOLVED

•         There is a risk to the welder/diver of electric shock. Precautions include achieving adequate electrical insulation of the welding equipment, shutting off the electricity supply immediately the arc is extinguished, and limiting the open-circuit voltage of MMA (SMA) welding sets. Secondly, hydrogen and oxygen are produced by the arc in wet welding.

•         Precautions must be taken to avoid the build-up of pockets of gas, which are potentially explosive. The other main area of risk is to the life or health of the welder/diver from nitrogen introduced into the blood steam during exposure to air at increased pressure. Precautions include the provision of an emergency air or gas supply, stand-by divers, and decompression chambers to avoid nitrogen narcosis following rapid surfacing after saturation diving.

•         For the structures being welded by wet underwater welding, inspection following welding may be more difficult than for welds deposited in air. Assuring the integrity of such underwater welds may be more difficult, and there is a risk that defects may remain undetected.

CONCLUSION

 

            Underwater welding is an important part of maintaining any metal structure existing in full or in part below the water. However, most conventional underwater welding systems have a number of problems. They're expensive, can provide only temporary repairs, dangerous, and/or hard to move around.

 

            Underwater welding techniques are most commonly used in executing marine engineering projects such as installation of oil and gas rigs. Underwater welding is mostly related to welding work pieces made from different types of metals such as steel, aluminum, copper, and others.

REFERENCES

1. D. J Keats, Manual on Wet Welding.

2.  Annon, Recent advances in dry underwater pipeline welding, Welding Engineer, 1974.

3.  Lythall, Gibson, Dry Hyperbaric underwater welding, Welding Institute.

4.  W.Lucas, International conference on computer technology in welding.

5.  Stepath M. D, Underwater welding and cutting yields slowly to research, Welding Engineer, April 1973.

6.  Silva, Hazlett, Underwater welding with iron – powder electrodes, Welding Journal, 1971.